Table of specific heat capacities

The following table of specific heat capacities gives the volumetric heat capacity, as well as the specific heat capacity of some substances and engineering materials, and (when applicable) the molar heat capacity.

Generally, the most constant parameter is notably the volumetric heat capacity (at least for solids), which is notably around the value of 3 megajoule per cubic meter and kelvin[1]:

${\displaystyle \rho c_{p}\simeq 3\,{\text{MJ/m}}^{3}{\text{K}}\quad {\text{(solid)}}}$

Note that the especially high molar values, as for paraffin, gasoline, water and ammonia, result from calculating specific heats in terms of moles of molecules. If specific heat is expressed per mole of atoms for these substances, none of the constant-volume values exceed, to any large extent, the theoretical Dulong–Petit limit of 25 J⋅mol⁻¹⋅K⁻¹ = 3 R per mole of atoms (see the last column of this table). Paraffin, for example, has very large molecules and thus a high heat capacity per mole, but as a substance it does not have remarkable heat capacity in terms of volume, mass, or atom-mol (which is just 1.41 R per mole of atoms, or less than half of most solids, in terms of heat capacity per atom).

In the last column, major departures of solids at standard temperatures from the Dulong–Petit law value of 3 R, are usually due to low atomic weight plus high bond strength (as in diamond) causing some vibration modes to have too much energy to be available to store thermal energy at the measured temperature. For gases, departure from 3 R per mole of atoms in this table is generally due to two factors: (1) failure of the higher quantum-energy-spaced vibration modes in gas molecules to be excited at room temperature, and (2) loss of potential energy degree of freedom for small gas molecules, simply because most of their atoms are not bonded maximally in space to other atoms, as happens in many solids.

Table of specific heat capacities at 25 °C (298 K) unless otherwise noted.

Notable minima and maxima are shown in maroon

Substance	Phase	Isobaric mass heat capacity cP J⋅g^−1⋅K^−1	Isobaric molar heat capacity CP,m J⋅mol^−1⋅K^−1	Isochore molar heat capacity CV,m J⋅mol^−1⋅K^−1	Isobaric volumetric heat capacity CP,v J⋅cm^−3⋅K^−1	Isochore atom-molar heat capacity in units of R CV,am atom-mol^−1
Air (Sea level, dry, 0 °C (273.15 K))	gas	1.0035	29.07	20.7643	0.001297	~ 1.25 R
Air (typical room conditions^A)	gas	1.012	29.19	20.85	0.00121	~ 1.25 R
Aluminium	solid	0.897	24.2		2.422	2.91 R
Ammonia	liquid	4.700	80.08		3.263	3.21 R
Animal tissue (incl. human)[2]	mixed	3.5			3.7*
Antimony	solid	0.207	25.2		1.386	3.03 R
Argon	gas	0.5203	20.7862	12.4717		1.50 R
Arsenic	solid	0.328	24.6		1.878	2.96 R
Beryllium	solid	1.82	16.4		3.367	1.97 R
Bismuth[3]	solid	0.123	25.7		1.20	3.09 R
Cadmium	solid	0.231	26.02			3.13 R
Carbon dioxide CO2[4]	gas	0.839*	36.94	28.46		1.14 R
Chromium	solid	0.449	23.35			2.81 R
Copper	solid	0.385	24.47		3.45	2.94 R
Diamond	solid	0.5091	6.115		1.782	0.74 R
Ethanol	liquid	2.44	112		1.925	1.50 R
Gasoline (octane)	liquid	2.22	228		1.64	1.05 R
Glass[3]	solid	0.84			2.1
Gold	solid	0.129	25.42		2.492	3.05 R
Granite[3]	solid	0.790			2.17
Graphite	solid	0.710	8.53		1.534	1.03 R
Helium	gas	5.1932	20.7862	12.4717		1.50 R
Hydrogen	gas	14.30	28.82			1.23 R
Hydrogen sulfide H2S[4]	gas	1.015*	34.60			1.05 R
Iron	solid	0.412	25.09[5]		3.537	3.02 R
Lead	solid	0.129	26.4		1.44	3.18 R
Lithium	solid	3.58	24.8		1.912	2.98 R
Lithium at 181 °C[6]	liquid	4.379	30.33		2.242	3.65 R
Magnesium	solid	1.02	24.9		1.773	2.99 R
Mercury	liquid	0.1395	27.98		1.888	3.36 R
Methane at 2 °C	gas	2.191	35.69			0.85 R
Methanol[7]	liquid	2.14	68.62			1.38 R
Molten salt (142–540 °C)[8]	liquid	1.56			2.62
Nitrogen	gas	1.040	29.12	20.8		1.25 R
Neon	gas	1.0301	20.7862	12.4717		1.50 R
Oxygen	gas	0.918	29.38	21.0		1.26 R
Paraffin wax C25H52	solid	2.5 (ave)	900		2.325	1.41 R
Polyethylene (rotomolding grade)[9][10]	solid	2.3027
Silica (fused)	solid	0.703	42.2		1.547	1.69 R
Silver[3]	solid	0.233	24.9		2.44	2.99 R
Sodium	solid	1.230	28.23			3.39 R
Steel	solid	0.466			3.756
Tin	solid	0.227	27.112		1.659	3.26 R
Titanium	solid	0.523	26.060		2.6384	3.13 R
Tungsten[3]	solid	0.134	24.8		2.58	2.98 R
Uranium	solid	0.116	27.7		2.216	3.33 R
Water at 100 °C (steam)	gas	2.080	37.47	28.03		1.12 R
Water at 25 °C	liquid	4.1813	75.327	74.53	4.1796	3.02 R
Water at 100 °C	liquid	4.1813	75.327	74.53	4.2160	3.02 R
Water at −10 °C (ice)[3]	solid	2.05	38.09		1.938	1.53 R
Zinc[3]	solid	0.387	25.2		2.76	3.03 R
Substance	Phase	Isobaric mass heat capacity cP J⋅g^−1⋅K^−1	Isobaric molar heat capacity CP,m J⋅mol^−1⋅K^−1	Isochore molar heat capacity CV,m J⋅mol^−1⋅K^−1	Isobaric volumetric heat capacity CP,v J⋅cm^−3⋅K^−1	Isochore atom-molar heat capacity in units of R CV,am atom-mol^−1

^A Assuming an altitude of 194 metres above mean sea level (the worldwide median altitude of human habitation), an indoor temperature of 23 °C, a dewpoint of 9 °C (40.85% relative humidity), and 760 mm–Hg sea level–corrected barometric pressure (molar water vapor content = 1.16%).
*Derived data by calculation. This is for water-rich tissues such as brain. The whole-body average figure for mammals is approximately 2.9 J⋅cm⁻³⋅K⁻¹ [11]

Mass heat capacity of building materials

See also: Thermal mass

(Usually of interest to builders and solar designers)

Mass heat capacity of building materials

Substance	Phase	cP J⋅g^−1⋅K^−1
Asphalt	solid	0.920
Brick	solid	0.840
Concrete	solid	0.880
Glass, silica	solid	0.840
Glass, crown	solid	0.670
Glass, flint	solid	0.503
Glass, pyrex	solid	0.753
Granite	solid	0.790
Gypsum	solid	1.090
Marble, mica	solid	0.880
Sand	solid	0.835
Soil	solid	0.800
Water	liquid	4.1813
Wood	solid	1.7 (1.2 to 2.9)
Substance	Phase	cP J g^−1 K^−1

See also

• List of thermal conductivities

References

1. Ashby, Shercliff, Cebon, Materials, Cambridge University Press, Chapter 12: Atoms in vibration: material and heat
2. Page 183 in: Cornelius, Flemming (2008). Medical biophysics (6th ed.). ISBN 978-1-4020-7110-2. (also giving a density of 1.06 kg/L)
3. "Table of Specific Heats".
4. Young; Geller (2008). Young and Geller College Physics (8th ed.). Pearson Education. ISBN 978-0-8053-9218-0.
5. Chase, M. W. (1998). "Iron". National Institute of Standards and Technology: 1–1951. Cite journal requires |journal= (help)
6. "Materials Properties Handbook, Material: Lithium" (PDF). Archived from the original (PDF) on September 5, 2006.
7. "HCV (Molar Heat Capacity (cV)) Data for Methanol". Dortmund Data Bank Software and Separation Technology.
8. "Heat Storage in Materials". The Engineering Toolbox.
9. Crawford, R. J. Rotational molding of plastics. ISBN 978-1-59124-192-8.
10. Gaur, Umesh; Wunderlich, Bernhard (1981). "Heat capacity and other thermodynamic properties of linear macromolecules. II. Polyethylene" (PDF). Journal of Physical and Chemical Reference Data. 10 (1): 119. Bibcode:1981JPCRD..10..119G. doi:10.1063/1.555636.
11. Faber, P.; Garby, L. (1995). "Fat content affects heat capacity: a study in mice". Acta Physiologica Scandinavica. 153 (2): 185–7. doi:10.1111/j.1748-1716.1995.tb09850.x. PMID 7778459.