Pilling–Bedworth ratio

The Pilling–Bedworth ratio (P–B ratio), in corrosion of metals, is the ratio of the volume of the elementary cell of a metal oxide to the volume of the elementary cell of the corresponding metal (from which the oxide is created).

On the basis of the P–B ratio, it can be judged if the metal is likely to passivate in dry air by creation of a protective oxide layer.

Definition

The P–B ratio is defined as:[1]

${\displaystyle \mathrm {R_{PB}={\frac {V_{oxide}}{V_{metal}}}={\frac {M_{oxide}\cdot \rho _{metal}}{n\cdot M_{metal}\cdot \rho _{oxide}}}} }$

where:

• ${\displaystyle R_{PB}}$ – Pilling–Bedworth ratio
• ${\displaystyle M}$ – atomic or molecular mass
• ${\displaystyle n}$ – number of atoms of metal per molecule of the oxide
• ${\displaystyle \rho }$ – density
• ${\displaystyle V}$ – molar volume

History

N.B. Pilling and R.E. Bedworth[2] suggested in 1923 that metals can be classed into two categories: those that form protective oxides, and those that cannot. They ascribed the protectiveness of the oxide to the volume the oxide takes in comparison to the volume of the metal used to produce this oxide in a corrosion process in dry air. The oxide layer would be unprotective if the ratio is less than unity because the film that forms on the metal surface is porous and/or cracked. Conversely, the metals with the ratio higher than 1 tend to be protective because they form an effective barrier that prevents the gas from further oxidizing the metal.[3]

Application

Scheme of the oxide structure and the Pilling-Bedworth ratio.

On the basis of measurements, the following connection can be shown:

• R_PB < 1: the oxide coating layer is too thin, likely broken and provides no protective effect (for example magnesium)
• R_PB > 2: the oxide coating chips off and provides no protective effect (example iron)
• 1 < R_PB < 2: the oxide coating is passivating and provides a protecting effect against further surface oxidation (examples aluminium, titanium, chromium-containing steels).

However, the exceptions to the above P-B ratio rules are numerous. Many of the exceptions can be attributed to the mechanism of the oxide growth: the underlying assumption in the P-B ratio is that oxygen needs to diffuse through the oxide layer to the metal surface; in reality, it is often the metal ion that diffuses to the air-oxide interface.

Values

Metal	Metal oxide	Formula	RPB
Potassium	Potassium oxide	K2O	0.474[4]
Sodium	Sodium oxide	Na2O	0.541[4]
Lithium	Lithium oxide	Li2O	0.567[4]
Strontium	Strontium oxide	SrO	0.611[4]
Calcium	Calcium oxide	CaO	0.64 [3]
Barium	Barium oxide	BaO	0.67[4]
Magnesium	Magnesium oxide	MgO	0.81
Aluminium	Aluminium oxide	Al2O3	1.28
Lead	Lead(II) oxide	PbO	1.28 [3]
Platinum	Platinum(II) oxide	PtO	1.56 [3]
Zirconium	Zirconium(IV) oxide	ZrO2	1.56
Zinc	Zinc oxide	ZnO	1.58
Hafnium	Hafnium(IV) oxide	HfO2	1.62 [3]
Nickel	Nickel(II) oxide	NiO	1.65
Iron	Iron(II) oxide	FeO	1.7
Titanium	Titanium(IV) oxide	TiO2	1.73
Iron	Iron(II,III) oxide	Fe3O4	1.90
Chromium	Chromium(III) oxide	Cr2O3	2.07
Iron	Iron(III) oxide	Fe2O3	2.14
Silicon	Silicon dioxide	SiO2	2.15
Tantalum	Tantalum(V) oxide	Ta2O5	2.47 [3]
Niobium	Niobium pentoxide	Nb2O5	2.69[4]
Vanadium	Vanadium(V) oxide	V2O5	3.25 [3]

References

1. Xu, C.; Gao, W. (2000). "Pilling-Bedworth ratio for oxidation of alloys". Mat. Res. Innovat. 3 (4): 231–235. doi:10.1007/s100190050008.
2. N.B. Pilling, R. E. Bedworth, "The Oxidation of Metals at High Temperatures". J. Inst. Met 29 (1923), p. 529-591.
3. "ASM Handbook Vol.13 Corrosion", ASM International, 1987
4. "Pilling–Bedworth ratios (PBRs) for metals and their oxides".