Lithium-ion capacitor

A lithium-ion capacitor (LIC) is a hybrid type of capacitor classified as a type of supercapacitor. Activated carbon is typically used as the cathode. The anode of the LIC consists of carbon material which is pre-doped with lithium ions. This pre-doping process lowers the potential of the anode and allows a relatively high output voltage compared with other supercapacitors.

Single-ended lithium-ion capacitors up to 200 F for PCB mounting
Lithium-ion capacitor
Specific energy11–14 Wh/kg
Energy density19–25 Wh/L
Specific power160–2800 W/kg
Charge/discharge efficiency95%
Self-discharge rate< 5% per month (temperature dependent)
Cycle durability>10,000
Nominal cell voltage2.2–3.8 V

History

In 1981, Dr. Yamabe of Kyoto University, in collaboration with Dr. Yata of Kanebo Co., created a material known as PAS (polyacenic semiconductive) by pyrolyzing phenolic resin at 400–700 °C.[1] This amorphous carbonaceous material performs well as the electrode in high-energy-density rechargeable devices. Patents were filed in the early 1980s by Kanebo Co.,[2] and efforts to commercialize PAS capacitors and lithium-ion capacitors (LICs) began. The PAS capacitor was first used in 1986,[3] and the LIC capacitor in 1991.

Concept
Hierarchical classification of supercapacitors and related types

A lithium-ion capacitor is a hybrid electrochemical energy storage device which combines the intercalation mechanism of a lithium-ion battery anode with the double-layer mechanism of the cathode of an electric double-layer capacitor (EDLC). The packaged energy density of an LIC is approximately 20 Wh/kg, roughly four times higher than an EDLC and five times lower than a lithium-ion battery. The power density, however, has been shown to match that of EDLCs, as it is able to completely discharge in seconds.[4] At the negative electrode (cathode), for which activated carbon is often used, charges are stored in an electric double layer that develops at the interface between the electrode and the electrolyte.

The positive electrode (anode) was originally made from lithium titanate oxide, but is now more commonly made from graphitic carbon to maximize energy density. The graphitic electrode potential initially at -0.1 V versus SHE (standard hydrogen electrode) is lowered further to -2.8 V by intercalating lithium ions. This step is referred to as "doping" and often takes place in the device between the anode and a sacrificial lithium electrode. The pre-doping process is critical to the device functioning as it can significantly affect the development of the solid electrolyte interphase (SEI) layer. Doping the anode lowers the anode potential and leads to a higher output voltage of the capacitor. Typically, output voltages for LICs are in the range of 3.8–4.0 V but are limited to minimum allowed voltages of 1.8–2.2 V. If the voltage drops any lower than this lithium ions will deintercalate more rapidly than they can be restored during normal use. Like EDLCs, LIC voltages vary linearly adding to complications integrating them into systems which have power electronics that expect the more stable voltage of batteries. As a consequence, LICs have a high energy density, which varies with the square of the voltage. The capacitance of the anode is several orders of magnitude larger than that of the cathode. As a result, the change of the anode potential during charge and discharge is much smaller than the change in the cathode potential.

Other candidate anode materials are being investigated as alternative to graphitic carbons[5], such as hard carbon[6][7][8], soft carbon, graphene-based carbons[9]. The expected benefit compared to graphitic carbons is in increasing the doped electrode potential improving power capability as well as safety in regard to metal plating.

The electrolyte used in an LIC is a lithium-ion salt solution that can be combined with other organic components and is generally identical to that used in lithium-ion batteries.

A separator prevents direct electrical contact between anode and cathode.

Properties

Typical properties of an LIC are

  • high capacitance compared to a capacitor, because of the large anode, though low capacity compared to a Li-ion cell
  • high energy density compared to a capacitor(14 Wh/kg reported[10]), though low energy density compared to a Li-ion cell
  • high power density
  • high reliability
  • operating temperatures ranging from −20 °C to 70 °C[11]
  • low self-discharge (<5% voltage drop at 25 °C over three months)[11]

Comparison to other technologies
Ragone plot comparing LIC to other technologies

Batteries, EDLC and LICs each have different strengths and weaknesses, making them useful for different categories of applications. LICs have higher power densities than batteries, and are safer than lithium-ion batteries, in which thermal runaway reactions may occur. Compared to the electric double-layer capacitor (EDLC), the LIC has a higher output voltage. Although they have similar power densities, the LIC has a much higher energy density than other supercapacitors.

The Ragone plot in figure 1 shows that LICs combine the high energy of LIBs with the high power density of EDLCs.

Cycle life performance of LICs is much better than batteries and is similar to EDLCs.

Applications

Lithium-ion capacitors are quite suitable for applications which require a high energy density, high power densities and excellent durability. Since they combine high energy density with high power density, there is no need for additional electrical storage devices in various kinds of applications, resulting in reduced costs.

Potential applications for lithium-ion capacitors are, for example, in the fields of wind power generation systems, uninterruptible power source systems (UPS), voltage sag compensation, photovoltaic power generation, energy recovery systems in industrial machinery, and transportation systems.

gollark: `|||||`
gollark: Useful in, er, no circumstances.
gollark: It would actually be almost as fast as a regular array, except some iteration/indexing would be slower.
gollark: Yes, that was my idea.
gollark: You just need to think outside the box.

References
  1. Proceedings Annual Meeting of the Physical Society of Japan (Yokohama) 31p-K-1, 1982, March
  2. Japanese patent application No. 56-92626,1981
  3. International Conference on Science and Technology of Synthetic Metals 1986, Kyoto
  4. Sivakkumar, S.R.; Pandolfo, A.G. (20 March 2012). "Evaluation of lithium-ion capacitors assembled with pre-lithiated graphite anode and activated carbon cathode". Electrochimica Acta. 65: 280–287. doi:10.1016/j.electacta.2012.01.076.
  5. Ding, Jia; Hu, Wenbin; Paek, Eunsu; Mitlin, David (28 June 2018). "Review of Hybrid Ion Capacitors: From Aqueous to Lithium to Sodium". Chemical Reviews. 118 (14): 6457–6498. doi:10.1021/acs.chemrev.8b00116. ISSN 0009-2665. PMID 29953230.
  6. Ajuria, Jon; Redondo, Edurne; Arnaiz, Maria; Mysyk, Roman; Rojo, Teófilo; Goikolea, Eider (4 August 2017). "Lithium and sodium ion capacitors with high energy and power densities based on carbons from recycled olive pits". Journal of Power Sources. 359: 17–26. Bibcode:2017JPS...359...17A. doi:10.1016/j.jpowsour.2017.04.107. ISSN 0378-7753.
  7. Schroeder, M.; Winter, M.; Passerini, S.; Balducci, A. (3 September 2013). "On the cycling stability of lithium-ion capacitors containing soft carbon as anodic material". Journal of Power Sources. 238: 388–394. doi:10.1016/j.jpowsour.2013.04.045. ISSN 0378-7753.
  8. Schroeder, M.; Menne, S.; Ségalini, J.; Saurel, D.; Casas-Cabanas, M.; Passerini, S.; Winter, M.; Balducci, A. (2 November 2014). "Considerations about the influence of the structural and electrochemical properties of carbonaceous materials on the behavior of lithium-ion capacitors". Journal of Power Sources. 266: 250–258. Bibcode:2014JPS...266..250S. doi:10.1016/j.jpowsour.2014.05.024. ISSN 0378-7753.
  9. Ajuria, Jon; Arnaiz, Maria; Botas, Cristina; Carriazo, Daniel; Mysyk, Roman; Rojo, Teofilo; Talyzin, Alexandr V.; Goikolea, Eider (1 September 2017). "Graphene-based lithium ion capacitor with high gravimetric energy and power densities". Journal of Power Sources. 363: 422–427. Bibcode:2017JPS...363..422A. doi:10.1016/j.jpowsour.2017.07.096. ISSN 0378-7753.
  10. "FDK To Begin Mass Production of High-Capacity Li-Ion Capacitors". 4 January 2009. Retrieved 23 July 2010.
  11. "ULTIMO Li-ion hybrid capacitor Spec Sheet" (PDF).
This article is issued from Wikipedia. The text is licensed under Creative Commons - Attribution - Sharealike. Additional terms may apply for the media files.