Fulleride

Fullerides are chemical compounds containing fullerene anions. Common fullerides are derivatives of the most common fullerenes, i.e. C₆₀ and C₇₀. The scope of the area is large because multiple charges are possible, i.e., [C₆₀]ⁿ⁻ (n = 1, 2...6), and all fullerenes can be converted to fullerides. The suffix "-ide" implies their negatively charged nature.

Cs₃C₆₀ crystal structure

Fullerides can be isolated as derivatives with a wide range of cations. Most heavily studied derivatives are those with alkali metals, but fullerides have been prepared with organic cations. Fullerides are typically dark colored solids that generally dissolve in polar organic solvents.

Structure and bonding

According to electronic structure calculations, the LUMO of C₆₀ is a triply degenerate orbital of t_1u symmetry. Using the technique cyclic voltammetry, C₆₀ can be shown to undergo six reversible reductions starting at −1 V referenced to the Fc⁺/Fc couple. Reduction causes only subtle changes in the structure and many derivatives exhibit disorder, which obscures these effects. Many fullerides are subject to Jahn–Teller distortion. In certain cases, e.g. [PPN]₂C₆₀, the structures are highly ordered and slight (10 pm) elongation of some C−C bonds is observed.[1]

Preparation

Fullerides have been prepared in various ways:

treating with alkali metals to give the alkali metal fullerides:

C₆₀ + 2 K → K₂C₆₀

treating with suitable organic and organometallic reducing agents, such as cobaltocene and tetrakisdimethylaminoethylene.
alkali metal fullerides can be subjected to cation metathesis. In this way the (bis(triphenylphosphine)iminium (PPN⁺) salts have been prepared, e.g. [PPN]₂C₆₀:[1]

K₂C₆₀ + 2 [PPN]Cl → [PPN]₂C₆₀ + 2 KCl

The fulleride salt ([K(crypt-222)]⁺)₂[C₆₀]²⁻ salt is synthesized by treating C₆₀ with metallic potassium in the presence of [2.2.2]cryptand.

Alkali metal derivatives

Critical temperatures (T_c) of the fulleride salts M₃C₆₀
Salt	T_c (K)
Na₃C₆₀	(non-superconducting)
K₃C₆₀	18
Rb₃C₆₀	28
Cs₃C₆₀	40

Particular attention has been paid to alkali metal (Na⁺, K⁺, Rb⁺, Cs⁺) derivatives of C₆₀³⁻ because these compounds exhibit physical properties resulting from intercluster interactions such as metallic behavior. In contrast, in C₆₀, the individual molecules interact only weakly, i.e. with essentially nonoverlapping bands. These alkali metal derivatives are sometimes viewed as arising by intercalation of the metal into C₆₀ lattice. Alternatively, these materials are viewed as n-doped fullerenes.[2]

Alkali metal salts of this trianion are superconducting. In M₃C₆₀ (M = Na, K, Rb), the M⁺ ions occupy the interstitial holes in a lattice composed of ccp lattice composed of nearly spherical C₆₀ anions. In Cs₃C₆₀, the cages are arranged in a bcc lattice.

In 1991, it was revealed that potassium-doped C₆₀ becomes superconducting at 18 K (−255 °C).[3] This was the highest transition temperature for a molecular superconductor. Since then, superconductivity has been reported in fullerene doped with various other alkali metals.[4][5] It has been shown that the superconducting transition temperature in alkaline-metal-doped fullerene increases with the unit-cell volume V.[6][7] As Cs⁺ is the largest alkali ion, caesium-doped fullerene is an important material in this family. Superconductivity at 38 K (−235 °C) has been reported in bulk Cs₃C₆₀,[8] but only under applied pressure. The highest superconducting transition temperature of 33 K (−240 °C) at ambient pressure is reported for Cs₂RbC₆₀.[9]

The increase of transition temperature with the unit-cell volume had been believed to be evidence for the BCS mechanism of C₆₀ solid superconductivity, because inter C₆₀ separation can be related to an increase in the density of states on the Fermi level, N(ε_F). Therefore, efforts have been made to increase the interfullerene separation, in particular, intercalating neutral molecules into the A₃C₆₀ lattice to increase the interfullerene spacing while the valence of C₆₀ is kept unchanged. However, this ammoniation technique has revealed a new aspect of fullerene intercalation compounds: the Mott transition and the correlation between the orientation/orbital order of C₆₀ molecules and the magnetic structure.[10]

Fourfold-reduced materials, i.e., those with the stoichiometry A₄C₆₀, are insulating, even though the t_1u band is only partially filled.[11] This apparent anomaly may be explained by the Jahn–Teller effect, where spontaneous deformations of high-symmetry molecules induce the splitting of degenerate levels to gain the electronic energy. The Jahn–Teller type electron-phonon interaction is strong enough in C₆₀ solids to destroy the band picture for particular valence states.[10]

A narrow band or strongly correlated electronic system and degenerated ground states are relevant to explaining superconductivity in fulleride solids. When the interelectron repulsion U is greater than the bandwidth, an insulating localized electron ground state is produced in the simple Mott–Hubbard model. This explains the absence of superconductivity at ambient pressure in caesium-doped C₆₀ solids.[8] Electron-correlation-driven localization of the t_1u electrons exceeds the critical value, leading to the Mott insulator. The application of high pressure decreases the interfullerene spacing, therefore caesium-doped C₆₀ solids turn to metallic and superconducting.

A fully developed theory of C₆₀ solids superconductivity is lacking, but it has been widely accepted that strong electronic correlations and the Jahn–Teller electron–phonon coupling[12] produce local electron pairings that show a high transition temperature close to the insulator–metal transition.[13]

gollark: I'll fix it.

gollark: This code is very well-designed and would simply spam me repeatedly.

gollark: See, there's nothing in the spec which says you have to actually answer HTTP requests in the shortest possible time. Not that I would obey it.

gollark: So it won't constantly spam me for requests.

gollark: The server keeps the connections open until it hits 30 seconds, or a message occurs.

References

Reed, Christopher A.; Bolskar, Robert D. (2000). "Discrete Fulleride Anions and Fullerenium Cations" (PDF). Chemical Reviews. 100 (3): 1075–1120. doi:10.1021/cr980017o.CS1 maint: uses authors parameter (link)
Gunnarsson, O. (1997). "Superconductivity in fullerides". Reviews of Modern Physics. 69 (2): 575–606. arXiv:cond-mat/9611150. Bibcode:1997RvMP...69..575G. doi:10.1103/RevModPhys.69.575.
Hebard, A. F.; Rosseinsky, M. J.; Haddon, R. C.; Murphy, D. W.; Glarum, S. H.; Palstra, T. T. M.; Ramirez, A. P.; Kortan, A. R. (1991). "Superconductivity at 18 K in potassium-doped C₆₀" (PDF). Nature. 350 (6319): 600–601. Bibcode:1991Natur.350..600H. doi:10.1038/350600a0.
Rosseinsky, M.; Ramirez, A.; Glarum, S.; Murphy, D.; Haddon, R.; Hebard, A.; Palstra, T.; Kortan, A.; Zahurak, S.; Makhija, A. (1991). "Superconductivity at 28 K in Rb_xC₆₀" (PDF). Physical Review Letters. 66 (21): 2830–2832. Bibcode:1991PhRvL..66.2830R. doi:10.1103/PhysRevLett.66.2830. PMID 10043627.
Chen, C.-C.; Kelty, S. P.; Lieber, C. M. (1991). "(Rb_xK_1−x)₃C₆₀ Superconductors: Formation of a Continuous Series of Solid Solutions". Science. 253 (5022): 886–8. Bibcode:1991Sci...253..886C. doi:10.1126/science.253.5022.886. PMID 17751824.
Zhou, O.; Zhu, Q.; Fischer, J. E.; Coustel, N.; Vaughan, G. B. M.; Heiney, P. A.; McCauley, J. P.; Smith, A. B. (1992). "Compressibility of M₃C₆₀ Fullerene Superconductors: Relation Between Tc and Lattice Parameter". Science. 255 (5046): 833–5. Bibcode:1992Sci...255..833Z. doi:10.1126/science.255.5046.833. PMID 17756430.
Brown, Craig; Takenobu, Taishi; Kordatos, Konstantinos; Prassides, Kosmas; Iwasa, Yoshihiro; Tanigaki, Katsumi (1999). "Pressure dependence of superconductivity in the Na₂Rb_0.5Cs_0.5C₆₀ fulleride". Physical Review B. 59 (6): 4439–4444. Bibcode:1999PhRvB..59.4439B. doi:10.1103/PhysRevB.59.4439.
Ganin, Alexey Y.; Takabayashi, Yasuhiro; Khimyak, Yaroslav Z.; Margadonna, Serena; Tamai, Anna; Rosseinsky, Matthew J.; Prassides, Kosmas (2008). "Bulk superconductivity at 38 K in a molecular system". Nature Materials. 7 (5): 367–71. Bibcode:2008NatMa...7..367G. doi:10.1038/nmat2179. PMID 18425134.
Tanigaki, K.; Ebbesen, T. W.; Saito, S.; Mizuki, J.; Tsai, J. S.; Kubo, Y.; Kuroshima, S. (1991). "Superconductivity at 33 K in Cs_xRb_yC₆₀". Nature. 352 (6332): 222–223. Bibcode:1991Natur.352..222T. doi:10.1038/352222a0.
Iwasa, Y; Takenobu, T (2003). "Superconductivity, Mott Hubbard states, and molecular orbital order in intercalated fullerides". Journal of Physics: Condensed Matter. 15 (13): R495. Bibcode:2003JPCM...15R.495I. doi:10.1088/0953-8984/15/13/202.
Erwin, Steven; Pederson, Mark (1993). "Electronic structure of superconducting Ba₆C₆₀". Physical Review B. 47 (21): 14657–14660. arXiv:cond-mat/9301006. Bibcode:1993PhRvB..4714657E. doi:10.1103/PhysRevB.47.14657.
Han, J.; Gunnarsson, O.; Crespi, V. (2003). "Strong Superconductivity with Local Jahn–Teller Phonons in C₆₀ Solids" (PDF). Physical Review Letters. 90 (16): 167006. Bibcode:2003PhRvL..90p7006H. doi:10.1103/PhysRevLett.90.167006. PMID 12731998.
Capone, M.; Fabrizio, M; Castellani, C; Tosatti, E (2002). "Strongly Correlated Superconductivity". Science. 296 (5577): 2364–6. arXiv:cond-mat/0207058. Bibcode:2002Sci...296.2364C. doi:10.1126/science.1071122. PMID 12089436.

Fulleride

Structure and bonding

Preparation

Alkali metal derivatives

References

Further reading