Dunt

Ceramics

Dunting is a fault that can occur during the firing of ceramic articles. It is the "cracking that occurs in fired ceramic bodies as a result of a thermally induced stress" [1] and is caused by a "ware cooled too quickly after it has been fired".[2][3]

Although usually occurring during cooling dunts can also be caused by excessively fast heating rates. Heating dunts can be recognised by rounded edges to the cracks as the glaze matured after they occurred, whereas cooling dunts have sharp edges.[4][5]

It has been found that bodies formulated with quartz rather than flint were more susceptible to dunting, especially on re-fire. It was postulated this may be related to the lower Young's modulus of the quartz based bodies.[6]

Dunting also occurs in wares produced from montmorillinite clay bodies due to the volume expansion of cristobalite during its inversion upon cooling. "The release of free silica, takes place in montmorillonite above 950 C, but almost double the silica is released, compared to kaolin. Therefore, clay bodies with high amounts of montmorillonite contain a high percentage of free silica after firing, which may cause the ware to crack during cooling.(Dunting)" [7]

gollark: I'm pretty sure this is an automated spambot swarm thing.
gollark: The banner is actually perfect and without flaw.
gollark: How did you find heavserver?
gollark: ↑ what they said, welcome to heavserver
gollark: This temporary departure has to stop!

See also

References
  1. "Standard Terminology of Ceramic Whitewares and Related Products." ASTM C242-01. ASTM International.
  2. "Dictionary of Ceramics", Third edition. A.Dodd A. D.Murfin. Institute of Materials. 1994. ISBN 0-901716-56-1
  3. "Dunting Temperature Measurement." K.Marshall, W.Roberts. British Ceramic Research Association. TN 143.1969.
  4. "Dictionary of Ceramics", Third edition. A.Dodd A. D.Murfin. Institute of Materials. 1994. ISBN 0-901716-56-1
  5. "Dunting - A Serious Problem Of Ceramics Industry." S.K.Mukherji. Indian Ceramics. 27, (2), 36, 1984.
  6. "Quartz V Flint. Pt.2. Aspects Related To Refire Dunting." K.Marshall, W.Roberts. British Ceramic Research Association. TN 141 Pt.2. 1969.
  7. "Clay Materials - For the self reliant potter", Henrik Norske. GTZ 1990; 98 pages
This article is issued from Wikipedia. The text is licensed under Creative Commons - Attribution - Sharealike. Additional terms may apply for the media files.